Flame retardant polycarbonate composition

ABSTRACT

A flame retardant polycarbonate composition comprising in admixture an aromatic carbonate polymer and a flame retardant additive which may be the metal salts of either monomeric or polymeric aromatic sulfonesulfonic acids, or mixtures thereof.

This invention is directed to a flame retardant polycarbonate composition and in particular an aromatic polycarbonate containing in admixture therewith a particular flame retardant additive which may be the metal salts of either monomeric or polymeric aromatic sulfonesulfonates, or mixtures of these.

BACKGROUND OF THE INVENTION

With the increasing concern for safety, there is a positive move towards providing safe materials for public and household use. One particular area of need is that of providing flame resistant or flame retardant products for use by the ultimate consumer. As a result of this demand, many products are being required to meet certain flame retardant criteria both by local and federal government and the manufacturers of such products. One particular set of conditions employed as a measuring standard for flame retardancy is set forth in Underwriters' Laboratories, Inc. Bulletin 94. This Bulletin sets forth certain conditions by which materials are rated for self-extinguishing characteristics.

In the art, there are many known flame retardant additives which are employed by mixing with products to render such materials self-extinguishing or flame retardant. Such flame retardant additives have been known to be employed in amounts of 5 to 20 weight percent in order to be effective in extinguishing burning of those products which are combustible. It has also been found that such amounts can have a degrading effect upon the base product to be rendered flame retardant, resulting in the losses of valuable physical properties of the base product. This is particularly so when employing known flame retardant additives with the base product polycarbonate resins. Many of these known additives have a degrading effect upon the polymer.

DESCRIPTION OF THE INVENTION

It has now been surprisingly discovered that an aromatic polycarbonate can be made flame retardant by incorporating with the aromatic polycarbonate minor amounts of certain additives, which additives are inert and do not degrade the aromatic polycarbonate. The particular additive employed herein is unique in that even very minor amounts render the aromatic polycarbonate flame retardant. The amount of the additive employed herein can vary, preferably, from 0.01 to about 10 weight percent based on the weight of the aromatic polycarbonate.

More specifically, the particular additive of this invention is the metal salt of either the monomeric or polymeric aromatic sulfonesulfonates or mixtures of these. The metal salt employed in the practice of this invention is either the alkali metal or alkali earth metal salt or mixtures of metal salts. The metals of these groups are sodium, lithium, potassium, rubidium, cesium, beryllium, magnesium, calcium, strontium and barium.

The aromatic sulfonesulfonates employed in the practice of this invention is a substituted or unsubstituted aromatic sulfonesulfonate wherein the substituent consists of an electron withdrawing radical. As employed herein and within the scope of this invention, any of the electron withdrawing radicals can be employed in the practice of this invention. However, preferably, the electron withdrawing radical or substituent employed in the practice of this invention is the halo-, nitro-, trihalomethyl and cyano electron withdrawing radicals or mixtures of these electron withdrawing radicals.

The electron withdrawing phenomenon, or as it is also referred to as electronegativity, is defined in Basic Principles of Organic Chemistry by Roberts and Caserio, 1964 (pages 185-186), and Physical Organic Chemistry by Jack Hine, McGraw-Hill Book Company, Inc. 1962 (pages 5, 32 and 85-93). Briefly, the electron withdrawing phenomenon is where the radical has a strong affinity for a negative charge, namely electrons, but still remains covalent and does not form an ion. This is an extremely brief description of this phenomenon and is merely set forth here to describe the electron withdrawing effect. Reference should be made to the texts set forth above.

In the practice of this invention, the types of aromatic sulfonesulfonates employed herein may be either the monomeric form or the polymeric form or mixtures of these. When first considering the monomeric form, the metal salt of the monomeric aromatic sulfonesulfonate can best be represented by the following formula:

    R'(SO.sub.2).sub.1-2 R"(SO.sub.3 M).sub.1-6 X.sub.0-11     I.

wherein X is an electron withdrawing radical, M is a metal which may be selected from the periodic table of either an alkali metal or an alkali earth metal, and R' and R" may be either an aryl radical of 1-2 aromatic rings or an aliphatic radical of 1-6 carbon atoms and they may be the same or different. It is to be understood, however, that R' and R" together must contain at least one aromatic ring.

When the polymeric form of the aromatic sulfonesulfonate is employed in the practice of this invention, the polymer consists of at least 2 repeating units in the following formula:

    --[AB].sub.m [CB].sub.n --.sub.p                           II.

in the above formula, B is an aromatic sulfone having the following formula ##SPC1##

and A and C are dioxy radicals having 1-2 aromatic rings and may be independently selected from ##SPC2##

In the above formulae, M is a metal which may be either an alkali metal or an alkali earth metal, R is an alkylene or alkylidene radical of 1-10 carbon atoms and y is an integer of from 0-4 providing that the sum of y when employed in Formula II is at least 1. In the above formulae, X is a halo electron withdrawing radical. As shown, the polymeric form of the additive may or may not have an electron withdrawing radical and if it is employed, the electron withdrawing radical is only a halo radical. Also, in Formula II, m is 1 and n is an integer of from 0-20 and p is an integer from 2-200.

Also, in the practice of this invention, the above units of [AB] and [CB] can be randomly selected while the polymer structure can be either a copolymer, a random copolymer, a block copolymer or a random-block copolymer or mixtures of these polymeric forms. In addition, the ratio of sulfonated aromatic rings to unsulfonated aromatic rings can vary from greater than 1 to 1 to as low as that which is necessary to render the polycarbonate flame retardant and this may be 1:100.

In the practice of this invention, there are many polymers that meet the requirements of Formula II above and which offer excellent flame retardant characteristics to an aromatic polycarbonate. The preferred polymeric additive employed in the practice of this invention has the following formula: ##SPC3##

Another preferred polymeric additive employed in the practice of this invention is one containing an electron withdrawing radical and has the following formula: ##SPC4##

PREFERRED EMBODIMENT OF THE INVENTION

In order to more fully and clearly illustrate the present invention, the following specific examples are presented. It is intended that the examples be considered as illustrative rather than limiting the invention disclosed and claimed herein. In the examples, all parts and percentages are on a weight basis unless otherwise specified.

EXAMPLE I

Ninety-nine parts of an aromatic polycarbonate, prepared by reacting 2,2-bis(4-hydroxyphenyl)propane and phosgene in the presence of an acid acceptor and a molecular weight regulator and having an intrinsic viscosity of 0.57 is mixed with 1 part of a finely ground dehydrated additive listed in Table I by tumbling the ingredients together in a laboratory tumbler. The resulting mixture is then fed to an extruder, which extruder is operated at about 265°C., and the extrudate is comminuted into pellets.

The pellets are then injection molded at about 315°C. into test bars of about 5 in. by 1/2 in. by about 1/16 -1/8 in. thick. The test bars (five for each additive listed in the Table) are subject to the test procedure set forth in Underwriters' Laboratories, Inc. Bulletin UL-94, Burning Test for Classifying Materials. In accordance with this test procedure, materials so investigated are rated either SE-0, SE-I or SE-II based on the results of 5 specimens. The criteria for each SE rating per UL-94 is briefly as follows:

"SE-0": Average flaming and/or glowing after removal of the igniting flame shall not exceed 5 seconds and none of the specimens shall drip flaming particles which ignite absorbent cotton.

"SE-I": Average flaming and/or glowing after removal of the igniting flame shall not exceed 25 seconds and the glowing does not travel vertically for more than one-eighth inch of the specimen after flaming ceases and glowing is incapable of igniting absorbent cotton.

"SE-II": Average flaming and/or glowing after removal of the igniting flame shall not exceed 25 seconds and the specimens drip flaming particles which ignite absorbent cotton.

In addition, a test bar which continues to burn for more than 25 seconds after removal of the igniting flame is classified, not by UL-94, but by the standards of the instant invention, as "burns". Further, UL-94 requires that all test bars in each test group must meet the SE type rating to achieve the particular classification. Otherwise, the five bars receive the rating of the worst single bar. For example, if one bar is classified as SE-II and the other four (4) are classified as SE-0, then the rating for all 5 bars is SE-II.

The results of the different additives within the scope of the instant invention are as follows with a control being the aromatic polycarbonate as prepared above without the additive of the type set forth herein.

                                      Table 1                                      __________________________________________________________________________                               Flame Out Time                                                                           No. of Drips                               Additive (1.0 weight percent)                                                                            Seconds (Avg.)                                                                           Per Test Bar                                                                            Rating                                                                              Remarks                      __________________________________________________________________________        CONTROL                31.6      4+       Burns                             Sodium salt of diphenylsulfone-3-                                                                        4.4       1.6      SE-II                             sulfonic acid                                                                  Sodium salt of 4,4'-dibromodiphenyl-                                                                     2.2       1.2      SE-II                                                                               2 test bars were SE-0        sulfone-3-sulfonic acid                                                        Calcium salt of 4-chloro-4'-nitrodi-                                                                     3.6       0.8      SE-II                                                                               2 test bars were SE-0        phenylsulfone-3-sulfonic acid                                                  Potassium salt of 4-chloro-3'-(tri-                                                                      2.8       0.8      SE-II                                                                               4 test bars were SE-0        fluoromethyl)diphenylsulfone-3-                                                sulfonic acid                                                                  Disodium salt of diphenylsulfone-3,3'-                                                                   4.0       1.0      SE-II                                                                               3 test bars were SE-I        disulfonic acid                                                                Disodium salt of 4,4'-dichlorodiphenyl-                                                                  3.7       0.8      SE-II                                                                               3 test bars were SE-0        sulfone-3,3'-disulfonic acid                                                   Disodium salt of 4,2',4',5'-tetrachloro-                                                                 3.9       1.0      SE-II                                                                               4 test bars were SE-0        diphenylsulfone-3,5-disulfonic acid                                            Calcium salt of 4,4'-dichloro-1,1'-                                                                      2.8       0        SE-0                              dinaphthylsulfone-5,5'-disulfonic acid                                         Polysodium salt of        3.6       0        SE-0                              Disodium salt of 1,5-dichlorothian-                                                                      3.2       1.0*     SE-0 *Non-flaming drip            threne-S,S'-tetroxide-x,y-disulfonic                                           acid                                                                           Polysodium salt of        4.8       0        SE-0                              Polysodium salt of        3.3       0        SE-0                              __________________________________________________________________________

EXAMPLE II

This Example is set forth to demonstrate the effect of the flame retardant additives of this invention at the lower limits of 0.01 weight percent based on the weight of the polymer composition.

In preparing the test bars for this Example, 99.99 parts of the polycarbonate of Example I is mixed with 0.01 weight percent of the additives listed in Table 2 employing the same procedure. Test bars are then molded using the same procedure employed in Example I. The test bars are subjected to the same test procedure of Example I with the following results:

                                      Table 2                                      __________________________________________________________________________                               Flame Out Time                                                                             No. of Drips                             Additive (0.01 weight percent)                                                                           Seconds (Avg.)                                                                             Per Test Bar                                                                              Rating Remarks                __________________________________________________________________________        CONTROL                31.6        4+         Burns                         Disodium salt of 4,2',4',5'-tetra-                                                                       8.6         3.6        SE-II                         chlorodiphenylsulfone-3,5-disulfonic                                           acid                                                                           Calcium salt of 4,4'-dichloro-1,1'-                                                                      9.6         3.6        SE-II                         dinaphthylsulfone-5,5'-disulfonic                                              acid                                                                           Polysodium salt of        7.2         4.0        SE-II                         __________________________________________________________________________

EXAMPLE III

This Example is set forth to show the effect of a known commercially available flame retardant additive.

Example I is repeated except that in place of the additives employed therein, only 1 part 1,2,5,6,9,10-hexabromocyclododecane is used herein. The results obtained upon evaluating five test bars are the same as obtained for the Control shown in Table 1 above.

B

Part A. above is repeated but using 5 weight percent of the above additive, namely 1,2,5,6,9,10-hexabromocyclododecane. The results obtained are the same as obtained in Part A. above.

C

Part A. above is repeated but using 10 weight percent of the above additive, namely 1,2,5,6,9,10-hexabromocyclododecane. At this level of additive, test bars are rated SE-II. However, the polycarbonate is badly degraded as evidenced by severe dark streaking of the molded test bars, which degradation does not occur with the additives of the instant invention.

EXAMPLE IV

Example III is repeated except that hexabromobiphenyl is employed herein. The results obtained are essentially the same as those of Example III.

EXAMPLE V

Example III is repeated except that the additive employed herein is a combination of antimony oxide and a material which is a mixture of polychlorinated biphenyl (Aroclor by Monsanto Company). The proportion of the ingredients of the additive employed in this example is based on 3 parts of chlorine per 1 part of antimony. The results obtained at 1 weight percent and 5 weight percent amounts are the same as in Example III.

However, at the higher amount, namely 10 weight percent, flame retardancy effect is noted, but with, again, severe degradation of the polycarbonate, as evidenced by the substantial reduction in the intrinsic viscosity of the molded test bars. As molded, the intrinsic viscosity of the test bars with 1 weight percent of the above additive is about 0.50. The intrinsic viscosity of the molded test bars containing 10 weight percent of the flame retardant additive of this Example is 0.253. This shows the severe degradation of the polycarbonate when employing this type of well known flame retardant.

In the practice of this invention, aromatic carbonate polymers are rendered flame retardant by the addition of certain particular additives which are the metal salts of substituted and unsubstituted monomeric or polymeric aromatic sulfonesulfonates and include mixtures of these. The amount of the additives employed in the practice of this invention may vary from 0.01 to up to that amount which after further increasing of such an amount does not materially increase the flame retardant properties of the carbonate polymer. This is generally up to about 10 weight percent based on the weight of the aromatic carbonate polymer but may be higher. The amount of the additive to be employed can also be a function of the degree of flame retardancy desired.

It is not exactly understood how the additive of this invention functions or how such minor amounts can act as an effective flame retardant for the aromatic carbonate polymer. Analysis of the composition of this invention after being subjected to a fire temperature of about 600°C. showed an unusually high percentage of remaining char. This leads one to hypothesize that the additive may act as a cross-linking agent when the aromatic carbonate polymer is subjected to fire temperatures. However, it is emphasized that this is only theory and should not be construed as actually occurring.

As indicated previously, the additive of the instant invention comprises the alkali or alkali earth metal salts of the monomeric or polymeric aromatic sulfonesulfonates and mixtures of these. While a great number of such salts are set forth in the tables of the Examples of the instant invention, these are only a representative sample of the additives of this invention. The sodium, calcium, magnesium, potassium, strontium, lithium, barium, rubidium and cesium salts of other aromatic sulfonesulfonic acids can be employed in place of those of the Example with the same effective flame retardancy being achieved. These other metal salts of aromatic sulfonesulfonic acids are

diphenylsulfone-4,4'-disulfonic acid, disodium salt

methylphenylsulfone-4-sulfonic acid, calcium salt

2,3,4,5,6-pentachlorodiphenylsulfone-4-sulfonic acid, sodium salt

2,7-dichlorodibenzothiophene-S-dioxide-4,5-disulfonic acid, dipotassium salt

1,8-dibromodibenzothioxin-S-dioxide-2,7-disulfonic acid, disodium salt

In the practice of this invention, the additive is generally prepared by well known methods in the art. For example, one such well known method involves taking an aromatic sulfone such as diphenylsulfone and subjecting it to sulfonation using either sulfuric acid, chlorosulfonic acid, fuming sulfonic acid or sulfur trioxide. These reactions can be carried out at room temperature or at elevated temperatures such as about 50°C. The salt is then prepared by adding the proper alkaline reagent in sufficient amount to make the neutral salt. The salt is then recovered by precipitation or by distillation of the solvent.

In the case of a halo- electron withdrawing substituent, such as trifluoromethyl electron withdrawing substituent, it is best to start with the prepared trifluoromethyl aromatic sulfone and then sulfonate as above, as well as preparing the salt thereof.

In the practice of this invention, any of the aromatic polycarbonates can be employed herein. However, particularly useful are the aromatic polycarbonates prepared by reacting a dihydric phenol, such as bisphenol-A (2,2'bis(4 hydroxyphenyl)propane) with a carbonate precursor. Typical of some of the dihydric phenols that may be employed in the practice of this invention are bis(4-hydroxyphenyl)methane, 2,2-bis(4-hydroxyphenyl)propane, 2,2-bis(4-hydroxy-3-methylphenyl)propane, 4,4-bis(4-hydroxyphenyl)heptane, 2,2-(3,5,3',5'-tetrachloro-4,4'-dihydroxydiphenyl)propane, 2,2-(3,5,3',5'-tetrabromo-4,4'-dihydroxydiphenyl)propane, (3,3'-dichloro-4,4'-dihydroxydiphenyl)methane. Other dihydric phenols of the bisphenol type are also available and are disclosed in U.S. Pat. Nos. 2,999,835, 3,028,365 and 3,334,154.

In addition, the reaction is carried out with the carbonate precursor in the presence of a molecular weight regulator, an acid acceptor and a catalyst. The preferred carbonate precursor generally employed in preparing carbonate polymers is carbonyl chloride. However, other carbonate precursors may be employed and this includes other carbonyl halides, carbonate esters or haloformates.

The acid acceptors, molecular weight regulators and catalysts employed in the process of preparing polycarbonates are well known in the art and may be any of those commonly used to prepare polycarbonates.

As stated previously, mixtures can be employed in the practice of this invention and are included within the scope herein. Mixtures consist of mixtures of the various metal salts of monomeric and polymeric aromatic sulfonesulfonates. The mixtures offer certain advantages such as SE-0 rating for five test bars and essentially no drips per test bar.

It will thus be seen that the objects set forth above among those made apparent from the preceding description are efficiently attained and since certain changes may be made in carrying out the above process and in the composition set forth without departing from the scope of this invention, it is intended that all matters contained in the above description shall be interpreted as illustrative and not in a limiting sense. 

What is claimed is:
 1. A flame retardant aromatic carbonate polymer composition comprising in admixture an aromatic carbonate polymer and a minor amount of a monomeric alkali metal and alkali earth metal aromatic, sulfonesulfonate, or mixtures thereof.
 2. The composition of claim 1 wherein the composition comprises in admixture 0.01 to about 10 weight percent of the monomeric alkali metal and alkali earth metal aromatic sulfonesulfonate or mixtures thereof based on the weight of the aromatic carbonate polymer composition.
 3. The composition of claim 1 wherein the metal salt has the following formula: ##SPC5##
 4. The composition of claim 1 wherein the monomeric metal aromatic sulfonesulfonates have the following formula:

    R'(SO.sub.2).sub.1 R"(SO.sub.3 M).sub.1-6 X.sub.0-11

wherein M is a metal selected from the group consisting of alkali metal and alkali earth metal, R' and R" are independently selected from the group consisting of aryl radicals of 1-2 aromatic rings and an aliphatic radical of 1-6 carbon atoms, provided, however, that R' and R" together must contain at least one aromatic ring to which the SO₃ M group is attached, and wherein X is an electron withdrawing radical.
 5. The composition of claim 4 wherein the metal salt is potassium diphenylsulfone-3-sulfonate.
 6. The composition of claim 4 wherein the metal salt is dipotassium diphenylsulfone-3,3'-disulfonate.
 7. The composition of claim 4 wherein the electron withdrawing radical is selected from the group consisting of halo-, nitro-, trihalomethyl- and cyano- radicals and mixtures thereof.
 8. The composition of claim 4 wherein the electron withdrawing radical is chlorine.
 9. The composition of claim 4 wherein the metal salt is disodium 4,2', 4', 5'-tetrachlorodiphenylsulfone-3,5-disulfonate.
 10. The composition of claim 4 wherein the metal salt is disodium diphenylsulfone-3,3'-disulfonate. 